Startseite / Products / Brass / Tubes / Round tubes / 3 x 0,45 x 5000 mm
3 x 0,45 x 5000 mm

CW508L, CuZn37 3 x 0,45 x 5000 mm

Artikelnummer:
1016958
Diameter
3 mm
Wall thickness
0,45 mm
Length
5000 mm
Temper
Hard
Gewicht
≈ 0,03 kg/m
CO2e (avg)
≈ 4,6 kg/kg
Verfügbarkeit
Auf Anfrage

CW508L, CuZn37

CuZn37 is the major brass alloy for the cold forming process. Even though brasses with lower Zinc content have better cold forming properties, CuZn37 is the most used alloy. Reasons for this are on the one hand economical due to lower price of Zinc compared to Copper, on the other hand the forming properties of this alloy meet the demand of many applications . The alloy type is listed in the USA by EPA to have good antimicrobial properties. Main Applications Fasteners Fasteners. Industrial Cold Headed Parts, Heat Exchanger Shells, Pump Cylinder Liners Casting Characteristics. Typical Application: Metal goods, Deep drawn parts, Components for the electrical industry, Stamped parts, Connectors.

Verfügbarkeit & Zwischenverkauf vorbehalten. Die dargestellten Gewichte basieren auf theoretischen Werten. Bei Fragen stehen wir Ihnen gerne zur Verfügung.

Technical Specifications

Legierungen

Al Cu Ni Fe Pb Sn
g/cm3 Max Min Max Max Max Max Max Rest
CW508L, CuZn37 8,4 0,05 62 64 0,3 0,1 0,1 0,1 Zn

Messing Eigenschaften

MeltingPoint Annealing
W/m*K µm/(m*K) min °C KN/mm2 %IACS Norms Min cm/106*°C
CW508L, CuZn37 120 20,4 916 110 26 EN 1652 450 650
CW508L, CuZn37 120 20,4 916 110 26 EN 12163 450 650