Startseite / Products / Aluminium / Bars / Round Bars / 130 x 3000 mm
130 x 3000 mm

EN AW-2011 130 x 3000 mm

Artikelnummer:
1001150
Diameter
130 mm
Length
3000 mm
Process
Extruded
Temper
T6
Gewicht
≈ 37,70 kg/m
CO2e (avg)
≈ 9,0 kg/kg
Verfügbarkeit
Lagerware

EN AW-2011

An aluminium and copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like an EN AW-2007, but it is a bit softer. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds and gives a shiny surface after treatment. It has a high strength against metal fatigue. The alloy has an inferior corrosion resistance, and it is not suitable for welding because of the high content of copper. It is possibly approved after the ROHS.

Verfügbarkeit & Zwischenverkauf vorbehalten. Die dargestellten Gewichte basieren auf theoretischen Werten. Bei Fragen stehen wir Ihnen gerne zur Verfügung.

Technical Specifications

Legierungen

Si Fe Cu Zn Bi Pb Other
g/cm3 Max Max Min Max Max Min Max Min Max Max Rest
EN AW-2011 2,84 0,4 0,7 5 6 0,3 0,2 0,6 0,2 0,4 0,15 Al

Aluminium Eigenschaften

MeltingPoint
W/m*K µm/(m*K) min °C max °C KN/mm2 %IACS
EN AW-2011 T3 152 23 540 645 72 39
EN AW-2011 T4 152 23 540 645 72 39
EN AW-2011 T6 172 23 540 645 72 45,5
EN AW-2011 T8 172 23 540 645 72 45,5

Table1

Dimension Tensile strength (Rm) MPa Proof stress (Rp0,2) Elongation Brinell Hardness Elongation A50mm
Min Max Rm N/mm2 MPa % min HBS % min
EN 755-2:2013 EN AW-2011 T6 - 75 310 230 8 110 6
EN 755-2:2013 EN AW-2011 T6 - 60 310 230 8 110 6
EN 755-2:2013 EN AW-2011 T6 75 200 295 195 6 110 -