EN AW-1050A 12 x 1520 x 3020 mm
Artikelnummer:
1103141
Dicke
12 mm
Width
1520 mm
Length
3020 mm
Temper
H111
Gewicht
≈ 148,73 kg/stk
CO2e (avg)
≈ 9,4 kg/kg
Verfügbarkeit
Lagerware
EN AW-1050A
It is the most pure form of aluminium and the most common plate alloy. The alloy has a good property regarding bending and welding, and it is suitable for surface treatment.
It contains 99.5 % aluminium, and they mainly produce it in thickness from 0.5 mm - 6 mm.
EN AW-1050A DDQ:
It contains 99,5% aluminum and is produced in a very soft temper, making it suitable for deep drawing applications. Mainly produced in thickness 1,00 mm, 1,25 m, 1,05 mm and 2,00 mm.
Verfügbarkeit & Zwischenverkauf vorbehalten. Die dargestellten Gewichte basieren auf theoretischen Werten. Bei Fragen stehen wir Ihnen gerne zur Verfügung.
Technical Specifications
Legierungen
| Si | Fe | Cu | Mn | Mg | Zn | Ti | Other | ||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| g/cm3 | Max | Max | Max | Max | Min | Max | Max | Max | Max | Rest | |
| EN AW-1050A | 2,7 | 0,25 | 0,4 | 0,05 | 0,05 | 0,05 | 0,05 | 0,07 | 0,05 | 0,03 | Al |
Aluminium Eigenschaften
| MeltingPoint | |||||||
|---|---|---|---|---|---|---|---|
| W/m*K | µm/(m*K) | min °C | max °C | KN/mm2 | %IACS | ||
| EN AW-1050A | Hx2 | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
| EN AW-1050A | Hx4 | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
| EN AW-1050A | Hx6 | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
| EN AW-1050A | Hx8 | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
| EN AW-1050A | Hx9 | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
| EN AW-1050A | O | 229 | 23,5 | 645 | 658 | 69 | 59,5 |
Table1
| Tensile strength (Rm) MPa | Proof stress (Rp0,2) | Elongation | Brinell Hardness | Thickness interval | Elongation A50mm | Bend radius 90° | Bend radius 180° | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Rm N/mm2 | MPa | % min | HBS | mm | % min | t | t | |||||
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | - | 20 | 0,2 | 0,5 | 20 | 0 | 0 |
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | - | 20 | 0,5 | 1,5 | 22 | 0 | 0 |
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | - | 20 | 1,5 | 3 | 26 | 0 | 0 |
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | - | 20 | 3 | 6 | 29 | 0,5 | 0,5 |
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | - | 20 | 6 | 12,5 | 35 | 1 | 1 |
| EN 485-2:2008 | EN AW-1050A | H111 | 65 | 95 | 20 | 32 | 20 | 12,5 | 80 | - | - | - |